Por favor, use este identificador para citar o enlazar este ítem: http://hdl.handle.net/10495/9147
Registro completo de metadatos
Campo DC Valor Lengua/Idioma
dc.contributor.authorArismendi Echavarría, Jorge Alberto-
dc.contributor.authorAgudelo Arismendi, Lina Patricia-
dc.contributor.authorMarín I., Juan Esteban-
dc.contributor.authorPeláez Vargas, Alejandro-
dc.contributor.authorEchavarría Velásquez, Alejandro Iván-
dc.contributor.authorRojas M., Catalina María-
dc.date.accessioned2018-03-01T21:42:28Z-
dc.date.available2018-03-01T21:42:28Z-
dc.date.issued2006-
dc.identifier.citationArismendi J, et al. Caracterización electroquímica de cuatro biomateriales metálicos de uso odontológico. Rev Fac Odontol Univ Antioq. 2006;17(2):46-57es_ES
dc.identifier.issn0121246X-
dc.identifier.issn21457670 E-
dc.identifier.urihttp://hdl.handle.net/10495/9147-
dc.descriptionEn la literatura médica se ha sugerido el uso de aleaciones con un mínimo de 50% de contenido de oro para minimizar la corrosión en la unión implante-restauración. Sin embargo, las implicaciones clínicas a largo plazo de la colocación de dos metales diferentes en restauraciones sobre implantes es aún desconocido. El objetivo de este estudio es realizar la caracterización electroquímica de cuatro biomateriales metálicos de uso odontológico para determinar la posibilidad de corrosión entre ellos cuando se ponen en contacto durante los procedimientos restauradores sobre implantes. Se realizó un estudio in vitro de tipo descriptivo, prospectivo y comparativo. Se trabajó con cuatro tipos de biomateriales metálicos: titanio comercialmente puro, tomando como muestra un implante SuperCAT® de la casa Lifecore (Lifecore Biomedical Inc., Chaska, MN.); metal altamente noble, con un colado que se realizó a partir de un pilar plástico tipo UCLA® (Lifecore Biomedical Inc., Chaska, MN), con aleación IPS d.sign 91® (Williams, Ivoclar Vivadent AG, Liechtenstein); aleación de metal base con un colado que se realizó a partir de un pilar plástico tipo UCLA® con aleación IPS d.sign 15®, y aleación de titanio (Ti6Al 4V), usando un aditamento protésico tipo COC® de la casa comercial Lifecore. Se hizo la caracterización electroquímica de las cuatro aleaciones metálicas mediante un potenciostato Bas Zähner, con una celda de tres electrodos, usando como electrodo de referencia el electrodo de Ag/AgCl, obteniendo tres curvas de polarización para cada grupo en su forma pasivada y sin pasivar. La lectura de las curvas potenciodinámicas realizadas en este estudio, con cuatro biomateriales metálicos, y tomando como criterio el potencial de corrosión, concluye un excelente comportamiento para la aleación de titanio y de metales altamente nobles. La mejor combinación, teniendo en cuenta los criterios de potencial de corrosión y corriente a potenciales anódicos, se da con el titanio comercialmente puro y la aleación de titanio.es_ES
dc.description.abstractThe use of alloys with a minimum of 50% gold-content to minimize the potential of corrosion or galvanism in the implant- restoration interface has been suggested in the literature. However, long – term implications of placing two different kinds of metal at this level is still unknown. The purpose of this study was to perform the electrochemical characterization of four metallic biomaterials used in dentistry, to determine the possibility of corrosion among them when placed in contact during restorative procedures on implant fixtures. A prospective, descriptive, comparative, In - Vitro study was made for this purpose. Four types of metallic biomaterials were compared: commercially pure titanium using as a sample a Super CAT® implant (Lifecore Biomedical Inc., Chaska, MN); highly - noble alloy with a cast made from an UCLA abutment (Lifecore Biomedical Inc., Chaska, MN) with an IPS d.sing® 91 alloy (Williams, Ivoclar Vivadent AG, Liechtenstein); metal-base alloy with a cast made from an UCLA abutment with an IPS d.sing® 15 alloy; titanium alloy (Ti6Al4V) using a Lifecore COC® prosthetic abutment. The electrochemical characterization was made using a Bas Zahner potentiostat, with a three – electrode setup, obtaining three polarization curves for each group in its passive and non passive forms. The results showed that the titanium alloy had the best electrochemical behavior in both passive and non-passive state, which led to the smallest passive currents. The lowest corrosion potential was obtained for the metal-base alloy, because it had the highest passive currents.es_ES
dc.format.extent46-57es_ES
dc.format.mimetypeapplication/pdfes_ES
dc.language.isoeses_ES
dc.publisherUniversidad de Antioquia, Facultad de Odontologíaes_ES
dc.type.hasversioninfo:eu-repo/semantics/publishedVersiones_ES
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.sourceinstname: Universidad de Antioquiaes_ES
dc.sourcereponame: Repositorio Institucional Universidad de Antioquiaes_ES
dc.sourceRevista Facultad de Odontología Universidad de Antioquiaes_ES
dc.subjectImplantes dentaleses_ES
dc.subjectImplant dentureses_ES
dc.subjectTitanioes_ES
dc.subjectTitaniumes_ES
dc.subjectMateriales biomédicoses_ES
dc.subjectBiomedical materialses_ES
dc.subjectPrótesises_ES
dc.subjectProsthesises_ES
dc.subjectCorrosión y anticorrosivoses_ES
dc.subjectCorrosion and anti-corrosiveses_ES
dc.titleCaracterización electroquímica de cuatro biomateriales metálicos de uso odontológicoes_ES
dc.typeinfo:eu-repo/semantics/articlees_ES
dc.publisher.groupGrupo de Investigación en Patología Oral, Periodoncia y Cirugía Alvéolo-Dentaria (POPCAD)es_ES
dc.relation.volumen17es_ES
dc.relation.numero2es_ES
dc.source.tituloRevistaAbreviadaRev Fac Odontol Univ Antioqes_ES
Aparece en las colecciones: CIFO (Centro de Investigaciones de la Facultad de Odontología)

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ArismendiJorge_2006_CaracterizacionElectroquimicaBiomateriales.pdfArticulo de Revista719,91 kBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons

 


Gestión de T.I. /Sistema de Bibliotecas / Universidad de Antioquia / Cl. 67 Nº 53 - 108 - Bloque 8 Conmutador: 219 51 51- 219 51 40 comunicacionessistemadebibliotecas@udea.edu.co Medellín - Colombia